Product Details:
Grain Shape | Angular |
Color | Black |
Material | Iron |
Grade | G 10 |
Size | 2.0-2.8 mm |
Hardness | 9 Mohs |
Grades | Grades | Average Grain Size in mm |
G 10 | G 80 | 2.0-2.8 |
G 9 | G 66 | 1.7-2.4 |
G 8 | G 55 | 1.4-2.0 |
G 7 | G 47 | 1.2-1.7 |
G 6 | G 39 | 1.0-1.4 |
G 5 | G 34 | 0.8-1.2 |
G 4 | G 24 | 0.6-1.0 |
G 3 | G 17 | 0.4-0.8 |
G 2 | G 12 | 0.3-0.6 |
G 1 | G 7 | 0.2-0.4 |
Abrasives | Chilled Iron Grit (C.I.Grit) |
Chemical analysis | Carbon 2.5 to 3.4% |
Mn 0.6 to 1.0% | |
Si 0.8 to 1.20% | |
P 0.15 to 0.45% | |
S 0.25 to 0.50% | |
Hardness | 750 to 860 HV |
Micro-Structure | Martensite completely fine & uniform |
Density | 7.5gm./ml |
Product Details:
Carbon | 2.5 to 3.4% |
Mn | 0.6 to 1.0% |
Si | 0.8 to 1.20% |
S | 0.25 to 0.50% |
P | 0.15 to 0.45% |
Hardness | 750 to 860 HV |
Density | 7.5 gm./ml |
Product Details:
Minimum Order Quantity | 100 Kilogram |
S | 2.5 to 3.4% |
Carbon | 0.25 to 0.50% |
Mn | 0.6 to 1.0% |
Si | 0.8 to 1.20% |
P | 0.15 to 0.45% |
Hardness | 750 to 860 HV |
Density | 7.5gm./ml |
Product Details:
Carbon | 2.5 to 3.4% |
Mn | 0.6 to 1.0% |
Si | 0.8 to 1.20% |
P | 0.15 to 0.45% |
S | 0.25 to 0.50% |
Hardness | 750 to 860 HV |
Density | 7.5gm./ml |